Low molecular weight conjugated nitrogen compounds and devices fabricated using the same

ABSTRACT

Disclosed herein are low molecular weight conjugated nitrogen compounds having linear conjugated chains, and devices fabricated using the conjugated nitrogen compounds as organic semiconductor materials, hole conducting materials, or light-emitting materials. The conjugated nitrogen compounds can be spin-coated at room temperature, are stable, and has superior electrical conductivity.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to low molecular weight conjugated nitrogen compounds and devices fabricated using the conjugated nitrogen compounds. More particularly, the present invention relates to low molecular weight conjugated nitrogen compounds having linear conjugated chains, and devices fabricated using the conjugated nitrogen compounds as organic semiconductor materials, hole conducting materials, or light-emitting materials.

2. Description of the Related Art

Recent research has been concentrated on low molecular weight organic materials, such as pentacene, as organic semiconductor materials, and some research groups have paid attention to high molecular weight organic materials.

Although low molecular weight organic materials, e.g., pentacene, have been reported to have a high charge carrier mobility and a high on/off current ratio (I_(on)/I_(off) ratio), they necessitate the use of expensive vacuum deposition apparatuses for fabricating devices and have a difficulty in forming fine patterns. Accordingly, low molecular weight organic materials are not attractive for the manufacture of large-area displays at low costs.

Unlike low molecular weight organic materials, polythiophene-based high molecular weight organic materials are easily formed into solutions, and can be formed into thin films by screen printing, ink-jet and roll printing techniques. For these reasons, it is reported that the high molecular weight organic materials have advantages in the manufacture of large-area displays at low costs.

However, since the high molecular weight organic materials have different oxidation potentials depending on their molecular weight distribution, which is a cause of instability, their application to the fabrication of devices presents considerable difficulties. In contrast, since the low molecular weight organic materials have a constant oxidation potential, they have been found to be advantageous in terms of stability.

On the other hand, low molecular weight materials, e.g., tris-(8-hydroxyquinoline)aluminum (Alq), and high molecular weight materials, e.g., polyphenylenevinylene (PPV) and polyalkylthiophene (PAT), have been known as light-emitting materials. Like the above-mentioned organic semiconductor materials, low molecular weight light-emitting materials cannot be spin-coated at room temperature, while high molecular weight light-emitting materials can be coated by spin coating at room temperature. High molecular weight light-emitting materials still have the problem of instability.

SUMMARY OF THE INVENTION

Therefore, the present invention has been made in view of the above problems of the prior art, and it is an object of the present invention to provide low molecular weight conjugated nitrogen compounds having linear conjugated chains as low molecular weight organic materials that can be spin-coated at room temperature and are stable when applied to the fabrication of devices, as well as have superior electrical conductivity.

In accordance with one aspect of the present invention, there is provided a low molecular weight conjugated nitrogen compound represented by Formula 1 below:

wherein L is a single bond or a vinylene group,

Ar is a C₃₋₃₀ aryl or heteroaryl group,

R¹ and R² are each independently selected from the group consisting of hydrogen; C₁₋₁₀ linear and branched alkyl groups; C₁₋₁₀ linear and branched alkoxy groups; C₁₋₁₀ linear and branched hydroxyalkyl groups; and C₋₁₀ linear and branched alkoxyalkyl groups,

m is an integer between 1 and 5, and

n is an integer between 1 and 3.

In accordance with another aspect of the present invention, there is provided a device fabricated using the low molecular weight conjugated nitrogen compound, as an organic semiconductor material, a hole conducting material or a light-emitting material, that can be spin-coated at room temperature and are stable when applied to the fabrication of the device, as well as have superior electrical conductivity.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other objects, features and other advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:

FIG. 1 is a UV-VIS absorption spectrum of a low molecular weight conjugated nitrogen compound synthesized in Preparative Example 1 of the present invention;

FIG. 2 is a cyclic voltammogram of a low molecular weight conjugated nitrogen compound synthesized in Preparative Example 1 of the present invention;

FIG. 3 is a graph showing the current-voltage (I-V) characteristics of a device fabricated in Example 1 of the present invention;

FIG. 4 is a graph showing the current-voltage (I-V) characteristics of a device fabricated in Example 2 of the present invention; and

FIG. 5 is an electroluminescence spectrum of a device fabricated in Example 2 of the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention will now be described in more detail with reference to the accompanying drawings.

The present invention provides a low molecular weight conjugated nitrogen compound represented by Formula 1 below:

wherein L is a single bond or a vinylene group,

Ar is a C₃-30 aryl or heteroaryl group,

R¹ and R² are each independently selected from the group consisting of hydrogen; C₁₋₁₀ linear and branched alkyl groups, C₁₋₁₀ linear and branched alkoxy groups, C₁₋₁₀ linear and branched hydroxyalkyl groups, and C₁₋₁₀ linear and branched alkoxyalkyl groups,

m is an integer between 1 and 5, and

n is an integer between 1 and 3.

The low molecular weight conjugated nitrogen compound of the present invention has a structure wherein three linear conjugated chains as side chains are bonded to one central nitrogen atom of the molecule. Since the conjugated nitrogen compound of the present invention has a low molecular weight, it has a constant oxidation potential and is thus stable. In addition, since the conjugated nitrogen compound of the present invention is highly soluble in organic solvents, it can be coated by previously known coating techniques. Furthermore, since the conjugated nitrogen compound of the present invention has low oxidation levels, it has superior electrical conductivity at low voltages.

A representative example of Ar in the low molecular weight conjugated nitrogen compound of Formula 1 according to the present invention is selected from the arylene and heteroarylene compounds of Formula 2 below: Formula 2

Thiophene, 3,4-ethylenedioxythiophene (EDOT), and phenyl are more preferred.

More specifically, the low molecular weight conjugated nitrogen compound of Formula 1 is preferably selected from the group consisting of compounds represented by Formulae 3 to 6 below:

-   -   wherein R is selected from the group consisting of hydrogen;         C₁₋₁₀ linear and branched alkyl groups; C₁₋₁₀ linear and         branched alkoxy groups; C₁₋₁₀ linear and branched hydroxyalkyl         groups; and C₁₀ linear and branched alkoxyalkyl groups;

wherein R is as defined in Formula 3;

wherein R is as defined in Formula 3; and

wherein R is as defined in Formula 3.

The low molecular weight conjugated nitrogen compound of the present invention can be synthesized by chemical or electrochemical oxidation and condensation using an organometallic compound of a transition metal, such as nickel or palladium, which are representative polymerization processes of heteroaromatic compounds.

More preferably, there can be used a palladium (0) compound of Formula 7 below: PdL₄  Formula 7

wherein L is a ligand selected from the group consisting of triphenylphosphine (PPh₃), triphenylarsine (AsPh₃), triphenylphosphite (P(OPh)₃), diphenylphosphinoferrocene (dppf), diphenylphosphino butane (dppb), acetate (OAc), and dibenzylideneacetone (dba); and

palladium (II) compounds of Formulae 8 and 9 below: PdL₂X₂  Formula 8

wherein L is as defined in Formula 7, and X is I, Br or Cl; and PdL₂  Formula 9

wherein L is as defined in Formula 7.

Specifically, the compound of Formula 3 is synthesized through the reaction routes shown in Reaction Scheme 1 below:

Further, the compounds of Formulae 4 to 6 are synthesized through the respective reaction routes shown in Reaction Schemes 2 to 4 below:

The substituents of the low molecular weight conjugated nitrogen compounds thus prepared can be controlled in order to facilitate a subsequent solution process. As a result, the low molecular weight conjugated nitrogen compounds can be coated at room temperature by already known coating techniques. Specifically, the conjugated nitrogen compounds can be formed into a thin film by screen printing, printing, spin coating, spin casting, dipping, and ink spraying.

The present invention also provides a device fabricated using the low molecular weight conjugated nitrogen compound as an organic semiconductor material, a hole conducting material, or a light-emitting material.

Specific examples of the device according to the present invention include organic thin film transistors (OTFTs), organic field effect transistors (OFETs), organic solar photovoltaic cells, and organic light emitting devices.

The low molecular weight conjugated nitrogen compound of the present invention can be used as a material for an organic semiconductor layer of an OTFT or OFET, a hole conducting layer of an organic solar photovoltaic cell, or a light-emitting layer or hole conducting layer of an OLED by processes known in the art.

The present invention will now be described in more detail with reference to the following examples. However, these examples are given for the purpose of illustration and are not to be construed as limiting the scope of the invention.

PREPARATIVE EXAMPLE 1 Preparation of Low Molecular Weight Conjugated Nitrogen Compound (1)

First, 1 g (2 mmol) of tris(4-bromophenyl)amine (Aldrich) was dissolved in 100 ml of toluene, and then 2.9 ml (4.5 eq.) of 2-tributylstannylthiophene and 27 mg (1.1%) of Pd(PPh₃)₄ were added thereto. The mixture was refluxed under a nitrogen atmosphere for 12 hours. The reaction mixture was allowed to cool to room temperature, washed with brine twice, and dried over MgSO₄. After the solvent was evaporated, the obtained residue was washed with petroleum ether (PE), and dried, affording 0.87 g (yield: 85%) of tris[4-(2-thienyl)phenyl]amine as a pale yellow solid.

¹H NMR (CDCl₃) δ (ppm): 7.50 (d, 2H) 7.20 (m, 2H) 7.10 (d, 2H) 7.08 (dd, 1H)

500 mg (1 mmol) of the tris[4-(2-thienyl)phenyl]amine was dissolved in 30 ml of 1,2-dichloroethane and DMF (0.37 g), and then 0.78 g (5 eq.) of POCl₃ was added thereto. The mixture was refluxed under a nitrogen atmosphere for 15 hours. To the reaction mixture were added 50 ml of methylene chloride and 100 ml of a saturated aqueous sodium acetate solution. The resulting mixture was stirred for 2 hours. The obtained organic phase was separated, washed with water, and dried over MgSO₄. The solvents were evaporated, and then the residue was purified by column chromatography, affording 0.53 g (yield: 90%) of tris[4-(5-formyl-2-thienyl)phenyl]amine as an orange solid.

¹H NMR (CDCl₃) δ (ppm): 9.90 (s, 1H, CHO) 7.70 (d, 1H) 7.60 (d, 1H) 7.30 (d, 2H) 7.20 (d, 2H)

140 mg (0.2 mmol) of the tris[4-(5-formyl-2-thienyl)phenyl]amine and 0.66 g (5 eq.) of diethyl {5-[(3,4-dihexyl-2-thienyl)-ethen-2-yl]-3,4-dihexyl-2-thienyl}}methylphosphonate were dissolved in 30 ml of anhydrous THF, and then potassium terthiobutyrate (120 mg) was added thereto under a nitrogen atmosphere. After the mixture was stirred for 1.5 hours, 120 ml of methylene chloride was added thereto. The obtained organic phase was washed with water, and dried over MgSO₄. The solvents were evaporated, and the residue was purified by column chromatography, affording 0.38 g (yield: 76%) of the final compound as a red oil.

¹H-NMR (CDCl₃) δ (ppm): 7.50 (d, 2H), 7.15 (d, 1H), 7.15 (d, 2H), 7.05 (d, 1H), 7.00 (d, 1H), 6.95 (m, 3H), 6.75 (s, 1H), 2.50 (m, 8H), 1.40 (m, 32H), 0.90 (m, 12H)

The UV-VIS absorbance and cyclic voltammogram (solvent: 0.10 M Bu₄NPF₆—CH₂Cl₂, scan rate: 100 mVs⁻¹) of the final compound were measured, and the results are shown in FIGS. 1 and 2, respectively. The graphs shown in FIGS. 1 and 2 demonstrate that the conjugated nitrogen compound absorbs UV-VIS light at a broad range of wavelengths and shows highly stable oxidation-reduction reactivity.

PREPARATIVE EXAMPLE 2 Preparation of Low Molecular Weight Conjugated Nitrogen Compound (2)

120 mg (0.25 mmol) of tris(4-bromophenyl)amine (Aldrich) was dissolved in 12 ml of toluene, and then 5″-hexyl-2-tributylstannyl-5,2′:5,2″-terthiophene (7.25 eq.) and 20 mg (5%) of Pd(PPh₃)₄ were added thereto. The mixture was refluxed under a nitrogen atmosphere for 16 hours. The reaction mixture was allowed to cool to room temperature. After the toluene was evaporated, the resulting residue was dissolved in methylene chloride. The obtained organic phase was washed with brine twice, and dried over MgSO₄. After the solvents were evaporated, the obtained residue was washed with petroleum ether (PE), and dried, affording 0.19 g (yield: 65%) of the final compound as an orange solid.

¹H-NMR (CDCl₃) δ (ppm) 7.48 (d, 2H), 7.14 (d, 2H), 7.13 (d, 1H), 7.08 (d, 1H), 7.03 (d, 1H), 6.96 (d, 1H), 6.94 (d, 1H), 6.66 (d, 1H), 2.81(t, 2H), 1.69(qt, 2H), 1.35(m, 6H), 0.93 (t, 3H)

PREPARATIVE EXAMPLE 3 Preparation of Low Molecular Weight Conjugated Nitrogen Compound (3)

300 mg (yield: 70%) of the final compound as an orange solid was prepared in the same manner as in Preparative Example 1, except that tris[4-5-(formyl-2-thienyl)phenyl]amine 300 mg and thienyl-2-methyl-diethyl phosphonate 549 mg were used.

¹H-NMR (CDCl₃) δ (ppm) 7.50 (d, 2H), 7.10 (d, 1H), 7.00 (d, 2H), 6.95 (d, 1H), 6.90 (d, 1H), 6.73 (d, 1H), 6.70 (d, 1H), 6.65 (m, 2H)

PREPARATIVE EXAMPLE 4 Preparation of Low Molecular Weight Conjugated Nitrogen Compound (4)

320 mg (0.67 mmol) of tris(4-bromophenyl)amine (Aldrich), 3.17 g (7 eq.) of 3′,4′-ethylenedioxy-5″-hexyl-2-tributylstannyl-5,2′:5,2″-terthiophene and 40 mg (5%) of Pd(PPh₃)₄ were dissolved in 30 ml of toluene. The mixture was refluxed under a nitrogen atmosphere for 15 hours. The reaction mixture was allowed to cool to room temperature. After the toluene was evaporated, the resulting residue was dissolved in methylene chloride. The obtained organic phase was washed with water, and dried over MgSO₄. After the solvents were evaporated, the obtained residue was washed with petroleum ether (PE) and dissolved in methylene chloride. PE was added to the solution to obtain a precipitate. The precipitate was filtered to afford 0.42 g (yield: 45%) of the final compound as a brown solid.

¹H-NMR (CDCl₃) δ (ppm): 7.50 (d, 2H), 7.16 (d, 2H), 7.12 (d, 2H), 7.03 (d, 1H), 6.69 (d, 1H), 4.39 (d, 4H), 2.80 (t, 2H), 1.68 (qt, 2H), 1.38 (m, 2H), 1.32(m, 4H), 0.89(t, 3H)

EXAMPLE 1 Fabrication of Device and Measurement of Photovoltaic Efficiency

An 80 nm-thick layer of a conductive polymer (Baytron P, Bayer) was formed on a glass substrate on which an ITO electrode was formed. Thereafter, the low molecular weight conjugated nitrogen compound synthesized in Preparative Example 1 was spin-cast on the conductive polymer layer to form a 100 nm-thick organic semiconductor layer. Then, a 60 nm-thick counter electrode made of aluminum was formed on the organic semiconductor layer to fabricate a device for the measurement of photovoltaic efficiency. The current-voltage characteristics were measured under AM 1.5 illumination conditions, and the results are plotted in FIG. 3. The photovoltaic efficiency of the device was measured to be 0.35% at a light intensity of 100 mW/cm², as calculated from the I-V curves shown in FIG. 3.

EXAMPLE 2 Fabrication of Device and Measurement of Electroluminescence Spectrum

A device was fabricated in the same manner as in Example 1, except that the low molecular weight conjugated nitrogen compound prepared in Preparative Example 4 was used. The current-voltage characteristics of the device were measured under the same conditions as in Example 1, and the results are shown in FIG. 4. In addition, the electroluminescence spectrum of the device was measured, and the results are shown in FIG. 5. The graphs shown in FIGS. 4 and 5 indicate that the conjugated nitrogen compound shows luminescence properties and has a low threshold voltage.

As apparent from the above description, the low molecular weight conjugated nitrogen compound of the present invention is a low molecular weight organic semiconductor compound having a novel structure. In addition, the conjugated nitrogen compound of the present invention can be spin-coated at room temperature, is stable, and is superior in electrical conductivity and luminescence efficiency. Therefore, the conjugated nitrogen compound of the present invention can be widely applied to the fabrication of organic thin film transistors (OTFTs), organic field effect transistors (OFETs), organic solar photovoltaic cells, and organic light emitting devices.

Although the preferred embodiments of the present invention have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims. 

1. A low molecular weight conjugated nitrogen compound represented by Formula 1 below:

wherein L is a single bond or a vinylene group, Ar is a C₃-30 aryl or heteroaryl group, R¹ and R² are each independently selected from the group consisting of hydrogen; C₁₋₁₀ linear and branched alkyl groups; C₁₋₁₀ linear and branched alkoxy groups; C₁₋₁₀ linear and branched hydroxyalkyl groups; and C₁-10 linear and branched alkoxyalkyl groups, m is an integer between 1 and 5, and n is an integer between 1 and
 3. 2. The conjugated nitrogen compound according to claim 1, wherein the Ar is selected from the compounds represented by Formula 2 below:


3. The conjugated nitrogen compound according to claim 1, wherein the conjugated nitrogen compound is selected from the group consisting of compounds represented by Formulae 3 to 6 below:

wherein R is selected from the group consisting of hydrogen; C₁₋₁₀ linear and branched alkyl groups; C₁₋₁₀ linear and branched alkoxy groups; C₁₋₁₀ linear and branched hydroxyalkyl groups; and C₁₋₁₀ linear and branched alkoxyalkyl groups,

wherein R is as defined in Formula 3,

wherein R is as defined in Formula 3, and

wherein R is as defined in Formula
 3. 4. An organic thin film transistor comprising the conjugated nitrogen compound according to claim 1 as a material for a channel layer.
 5. The organic thin film transistor according to claim 4, wherein the material for a channel layer is formed into a thin film by screen printing, printing, spin coating, spin casting, dipping, or ink spraying.
 6. A solar photovoltaic cell comprising the conjugated nitrogen compound according to claim 1 as a hole conducting material.
 7. The solar photovoltaic cell according to claim 6, wherein the hole conducting material is formed into a thin film by screen printing, printing, spin coating, spin casting, dipping, or ink spraying.
 8. An organic light-emitting transistor comprising the conjugated nitrogen compound according to claim 1 as a light-emitting material or a hole conducting material.
 9. The organic light-emitting transistor according to claim 8, wherein the light-emitting material or hole conducting material is formed into a thin film by screen printing, printing, spin coating, spin casting, dipping, or ink spraying. 